Carbons from second generation biomass as sustainable supports for catalytic systems
2018
In this study activated carbons were produced from the wood of three different wood species (pine, birch, spruce). The resulting activated carbons were characterized in bulk for ash content, carbon content (elemental analyses), specific surface area, and pore size distribution, and at the surface by measuring the autogenerated pH and studying their structure by XPS. All the samples presented high surface areas and appeared to be mesoporous materials (mesopores >80%). The carbons were then used as support for AuPt nanoparticles and tested in the liquid phase oxidation of glycerol (GLY) and in the hydrogenation of levulinic acid (LA), two important chemicals from cellulose-based biomass. The …
Influence of a major exposure surface on the development of microporous micritic limestones - Example of the Upper Mishrif Formation (Cenomanian) of …
2017
18 pages; International audience; Microporous platform top limestones of the Cenomanian Mishrif Formation (offshore Qatar) were studied in order to investigate the diagenetic processes associated with the top-Mishrif subaerial unconformity and its influence on the development of microporosity in underlying carbonates. Petrographical and stable isotope results indicate that complex diagenetic changes occurred during subaerial exposure of the Mishrif Formation, including pervasive dissolution and meteoric cementation, as well as neomorphism of the micritic matrix. Micrites at the top of the Mishrif Formation are coarse (i.e. > 2 μm), sub-rounded and very dull luminescent under cathodoluminesc…
Pd nanoparticles immobilized on the poly-dopamine decorated halloysite nanotubes hybridized with N-doped porous carbon monolayer: A versatile catalys…
2020
A hybrid catalyst, Pd@Hal-pDA-NPC, with the utility for promoting both C–C coupling reactions (Sonogashira, Heck and Suzuki reactions) and hydrogenation of nitrocompounds is prepared through two main steps. First, Pd(0) nanoparticles was immobilized on the poly-dopamine decorated halloysite nanotubes (Hal-pDA) and then Pd@Hal-pDA was hybridized with the layers of a novel multi-N-doped porous carbon monolayer derived from 4,4′,4″-((1,3,5-triazine-2,4,6-triyl)tris(azanediyl))tribenzonitrile. The results established that the catalyst could catalyze all the reactions efficiently under mild reaction condition. Moreover Pd@Hal-pDA-NPC exhibited high recyclability (up to ten reac…
One-Dimensional Porous Carbon/Platinum Composites for Nanoscale Electrodes
2007
A simple approach towards one-dimensional mesoporous carbon with superior electrochemical capacitive activity.
2009
One-dimensional (1D) mesoporous carbons with highly ordered 3D interconnected pore structure and large-diameter pore size (10–20 nm) have been synthesized by a simple precursor-controlled thermolysis approach; such unique carbonaceous frameworks show superior capacitive behavior in electrochemical double-layer capacitors.
Carbons from second generation biomass as sustainable supports for catalytic systems
2018
Abstract In this study activated carbons were produced from the wood of three different wood species (pine, birch, spruce). The resulting activated carbons were characterized in bulk for ash content, carbon content (elemental analyses), specific surface area, and pore size distribution, and at the surface by measuring the autogenerated pH and studying their structure by XPS. All the samples presented high surface areas and appeared to be mesoporous materials (mesopores >80%). The carbons were then used as support for AuPt nanoparticles and tested in the liquid phase oxidation of glycerol (GLY) and in the hydrogenation of levulinic acid (LA), two important chemicals from cellulose-based biom…
Activated Carbon Production from Peat Using ZnCl2 : Characterization and Applications
2017
The process for producing activated carbon from peat was optimized. The peat was impregnated with different ratios of ZnCl2, and the impregnated biomass was activated at different temperatures. The specific surface area, pore size distribution, total carbon content, and yield of the activated carbon were investigated. The best results for the specific surface area and mesoporosity of the activated peat were obtained by using a high impregnation ratio (2) and high activation temperature (1073 K). Highly porous activated carbon was produced that had a specific surface area of approximately 1000 m2/g and total pore volume that was higher than 0.5 cm3/g for most samples. The activated carbon ha…